Si 이론적 용량 4,200mAh/g,
흑연의 이론용량 372mAh/g 약 10배
Si 및 흑연을 혼합함에 따른 효율 증대
균일한 탄소 코팅을 통한 장수명
실리콘을 통한 흑연 대비
더 빠른 충전 시간 및 높은 에너지 밀도
Product | GP10E | GP13 | GP13H | GP15 | GP18 |
---|---|---|---|---|---|
Capacity (mAh/g) |
< 1,000 | 1,300 | 1,300 | 1,500 | 1,800 |
Particle Size (µm) |
9.5 | 6.0 | 9.5 | 9.5 | 9.5 |
Capacity | 1,300 ± 50 mAh/g |
---|---|
High initial efficiency (Half cell) |
88 ~ 90% |
Long-term cycle | 92.3% @100Cycles |
Low-cost process | Low temp. &Eco-friendly |
---|---|
Particle size(D50, µm) | 9.5 ± 1.0µm |
Tap density | 1.0 ± 0.15g/cc |
Surface area | < 10.0m2/g |
Capacity | 1,500 ± 50 mAh/g |
---|---|
High initial efficiency (Half cell) |
87 ~ 89% |
Long-term cycle | 90.2% @100Cycles |
Low-cost process | Low temp. &Eco-friendly |
---|---|
Particle size(D50, µm) | 9.5 ± 1.0µm |
Tap density | 1.0 ± 0.15g/cc |
Surface area | < 10.0m2/g |
Capacity | 1,800 ± 50 mAh/g |
---|---|
High initial efficiency (Half cell) |
84 ~ 86% |
Low-cost process | Low temp. &Eco-friendly |
---|---|
Particle size(D50, µm) | 9.5 ± 1.0µm |
Tap density | 1.0 ± 0.15g/cc |
Surface area | < 10.0m2/g |